Dental restoration, method for production thereof and glass ceramic

ABSTRACT

The invention relates to glass ceramics, which show high strength, high translucency, high chemical stability and which are still mechanically processible. The invention further refers to a method for producing a dental restoration comprising such glass or glass ceramic as well as the dental restoration itself.

The invention relates to glass ceramics, which show high strength, high translucency, high chemical stability and which are still mechanically processible. The invention further refers to a method for producing a dental restoration comprising such glass or glass ceramic as well as the dental restoration itself.

In the lithium oxide-silicon dioxide system, lithium disilicate (Li₂O.2 SiO₂ (Li₂Si₂O₅))-glass ceramics are well known from the literature and several patents are based on this glass ceramic system. In EP 0 536 479 B1, self-glazed lithium disilicate glass ceramic objects are thus described for the production of tableware and, in EP 0 536 572 B1, lithium disilicate glass ceramics which can be used by scattering a fine-particle coloured glass onto the surface thereof as cladding elements for building purposes.

A main focus of the publications about lithium disilicate glass ceramics resides in dental applications. The lithium disilicate system is very suitable here for the production of CAD/CAM-processible glass ceramics since the crystallisation is effected here via the lithium metasilicate phase (see S. D. Stookey: “Chemical Machining of Photosensitive Glass”, Ind. Eng. Chem., 45, 115-118 (1993) and S. D. Stookey: “Photosensitively Opacifiable Glass” U.S. Pat. No. 2,684,911 (1954)).

These lithium metasilicate glass ceramics have such low strengths in this intermediate stage that they can be readily processed by means of CAD/CAM (M.-P. Borom, A. M. Turkalo, R. H. Doremus: “Strength and Microstructure in Lithium Disilicate Glass Ceramics”, J. Am. Ceram. Soc., 58, No. 9-10, 385-391 (1975) and DE 24 51 121 A1.

Only by the subsequent conversion to lithium disilicate or the growing of lithium metasilicate crystals, in a second heat treatment, dental materials with high strength are achieved.

The heat treatment which is carried out in a dental laboratory or in the dental practice is a burden for a technician as well as for the patient with respect to time and costs. In particular, during the chairside method, inconvenient waiting times can occur.

In this method, an individually adapted crown/onlay/inlay is milled out of a glass ceramic block after the first crystallisation stage by means of CAD/CAM, in the dental practice this is subjected to the second crystallisation stage in a special oven and used directly in the first and only dentist's visit for the patient (DE 10 2005 028 637).

Such a heat treatment requires an oven and the corresponding acquisition and maintenance costs. Moreover, such a heat treatment can be the source for defects of the final product. Another drawback is the required time for such treatment which is between 30 and 60 minutes. For common CAD/CAM-systems, a maximum strength of 170 MPa is the limit. Thus, the machineable materials cannot be directly used for high quality applications. The machineability is not only dependent on the strength of the material, but also dependent on further properties, such as the hardness, the modulus of elasticity, the fracture toughness as well as the structure and microstructure of the glass ceramic. It has to be differentiated between intercrystalline and trans-crystalline fraction formes.

Starting herefrom, it was the object of the present invention to provide glass ceramics which have improved strength values and also improved translucence and chemical resistance.

This object is achieved by the method for producing a dental restoration having the features of claim 1, the translucent and tooth coloured glass ceramic having the features of claim 11 and the dental restoration of claim 14. The further dependent claims reveal advantageous developments.

Within the scope of the present invention, glass compositions were developed in the basic system SiO₂—Li₂O—ZrO₂, which have lithium metasilicate as only or as main crystal phase (>50%).

It was surprisingly found that the use of specific lithium metasilicate compositions together with specific heat treatments for its crystallisation can result in finally crystallized glass ceramics with a high strength which can be machined with CAD/CAMtechniques.

It was shown in addition that up to 20% by weight of ZrO₂ can be incorporated in the glass without the structure being significantly influenced. Contrary to all expectations, the ZrO₂ does not hereby crystallise as a separate crystal phase but remains completely or extensively in the amorphous residual glass phase. Because of the high proportion of ZrO₂, the mechanical and chemical resistances are hugely improved in this amorphous phase, which also leads to improved properties in the entire dental glass ceramic (crystal phase(s) and residual glass phase), such as for example final strength and acid solubility.

The method is also suitable for a two-stage production process from the initial glass, a partial crystallisation of the lithium metasilicate being effected in the first processing stage, which enables good CAD/CAM processing. In the second processing stage, an increase in the crystal phase proportion (primary lithium metasilicate) is effected, which leads to the high strength values. The most important cause of the surprisingly high strengths in the lithium metasilicate system is hereby ascribed to the high zirconium oxide proportion (>8 MA).

High translucence is ensured via the low crystallite size in the glass ceramics. In addition, good chemical stability is ensured by the high zirconium oxide proportion in the glass phase.

According to the present invention, a method for producing a dental restoration comprising a lithium silicate glass ceramic is provided having the following steps:

-   a) an amorphous glass is subjected to at least one heat treatment     with temperatures from 450 to 1100° C. resulting in a translucent     and tooth coloured glass ceramic with a strength of at least 250 MPa     (measured according to DIN ISO 6872) and with the colour of tooth,     wherein during the at least one heat treatment at least a partial     crystallisation occurs due to the increased temperatures, and -   b) the glass ceramic is formed to a dental restoration for immediate     dental application and with a strength of at least 200 MPa (measured     according to DIN ISO 6872) by using a material removing process.

In the context of the present invention a translucent glass ceramic is a ceramic which has a transmission of light with a wavelength between 360 nm to 740 nm (measured according to DIN EN 410 with a spectrophotometer Minolta CM-3610d).

The tooth colour is determined in accordance with existing dental shade guides, e.g. Vita classical shade guide, Vita 3D master shade guide).

The stabilizer is preferably ZrO₂ and/or HfO₂. Preferably, the stabiliser is essentially present in an amorphous state.

There may be contained as additives components selected from the group consisting of nucleation agents, fluorescent agents, dyes, in particular glass-colouring oxides, coloured pigments and mixtures thereof, in the glass or in the glass ceramic.

The nucleating agents are preferably selected from the group consisting of phosphorous oxide, titanium oxide, tin oxide, mixtures thereof, and noble metals, preferably in an amount of 1 to 10 wt-%, more preferably 2 to 8 wt-% and most preferably 4 to 8 wt-%.

The fluorescent agents are preferably selected from the group consisting of oxides of bismuth, rare earth elements as neodymium, praseodymium, samarium, erbium, and europium, and mixtures thereof, preferably in an amount of 0.1 to 5 wt-%, more preferably 0.5 to 4 wt-% and most preferably 1 to 3 wt-%.

The glass colouring oxides are preferably selected from the group of oxides of iron, titanium, cerium, copper, chromium, cobalt, nickel, manganese, selenium, silver, indium, gold, vanadium, rare earth elements as neodymium, praseodymium, samarium, europium, terbium, dysprosium, holmium, erbium, yttrium, and mixtures thereof, preferably in an amount of 0.1 to 6 wt-%, more preferably 0.5 to 5 wt-% and most preferably 1 to 4 wt-%.

The coloured pigments can be doped spinels, which are comprised preferably in an amount of 0.1 to 6 wt-%, more preferably 0.5 to 5 wt-% and most preferably 1 to 4 wt-%.

Further additives are preferably selected from the group consisting of boron oxide, phosphorus oxide, fluorine, barium oxide, strontium oxide, magnesium oxide, zinc oxide, calcium oxide, yttrium oxide, titanium oxide, niobium oxide, tantalum oxide, lanthanum oxide and mixtures thereof, which are comprised preferably in an amount of 0.1 to 5 wt-%.

In a preferred embodiment, the amorphous glass has the following composition:

55 to 70 wt-% SiO₂, 10 to 25 wt-% Li₂O, 8 to 20 wt-% of a stabiliser selected from the group consisting of the oxides of Zr, Hf, Ge, La, Y, Ce, Ti, Zn or its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, and 0 to 20 wt-% additives. In a further preferred embodiment, the amorphous glass has the following composition: 55 to 70 wt-% SiO₂, 10 to 25 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, and 0 to 20 wt-% additives.

In a further preferred embodiment, the amorphous glass has the following composition:

55 to 64 wt-% SiO₂, 15 to 22 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0.1 to 8 wt-% Al₂O₃, 0 to 8 wt-% K₂O and/or Na₂O, and 0 to 15 wt-% additives.

In a further preferred embodiment, the amorphous glass has the following composition:

55 to 64 wt-% SiO₂, 17 to 20 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0.1 to 5 wt-% Al₂O₃, 0.1 to 5 wt-% K₂O and/or Na₂O, 2 to 8 wt-% P₂O₅, and 0 to 10 wt-% additives.

In a further preferred embodiment, the heat treatment is a single-stage treatment with a temperature from 600° C. to 950° C., preferably 780 to 900° C. It is another preferred embodiment that the heat treatment is a double-stage treatment with a first temperature from 600 to 800° C. and a second temperature from 780 to 900° C.

The lithium silicate glasses or glass ceramics according to the invention are used as dental material or as component of a dental material.

The material removing process is a subtractive process, preferably selected from the group consisting of milling, grinding, and laser ablation, preferably as a CAM process.

In a further preferred embodiment, the dental restoration is subjected to a finishing process before the dental application. Such a finishing process can be a polishing, a glazing, a sealing, a coating, and a veneering with a veneering ceramic or glaze.

The dental restoration is preferably an inlay, an onlay, a bridge, an abutment, a facing, a veneer, a facet, a crown, a partial crown, a framework or a coping.

According to the present invention, also a translucent and tooth coloured glass ceramic with a strength of at least 250 MPa (measured according to DIN ISO 6872) having the following composition is provided:

55 to 70 wt-% SiO₂, 10 to 25 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of Zr, Hf, Ge, La, Y, Ce, Ti, Zn or its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, and 0 to 20 wt-% additives.

In a preferred embodiment, the glass ceramic has the following composition:

55 to 70 wt-% SiO₂, 10 to 25 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, and 0 to 20 wt-% additives.

Preferably, the glass ceramic has the following composition:

55 to 64 wt-% SiO₂, 15 to 22 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0.1 to 8 wt-% Al₂O₃, 0 to 8 wt-% K₂O and/or Na₂O, and 0 to 15 wt-% additives.

In a further preferred embodiment, the glass ceramic has the following composition:

55 to 64 wt-% SiO₂, 17 to 20 wt-% Li₂O, 8 to 20 wt-% of a stabiliser from a group selected of ZrO₂, HfO₂ or its mixtures, 0.1 to 5 wt-% Al₂O₃, 0.1 to 5 wt-% K₂O and/or Na₂O, 2 to 8 wt-% P₂O₅, and 0 to 10 wt-% additives.

The glass ceramic has preferably a dimensional stability which allows the machining of the glass ceramic with a material removing process.

According to the present invention, furthermore, a dental restoration is provided which is producible by the above described method.

It is preferred that the dental restoration has a degree of crystallization of at least 5%, preferably at least 50%.

It is further preferred that the dental restoration has a strength of at least 200 MPa, preferably at least 300 MPa.

The dental restoration can have a finishing. Such a finishing is preferably a polishing, a glazing, a sealing, a coating, and a veneering with a veneering ceramic or glaze. Such a finished dental restoration has preferably a strength of at least 250 MPa, preferably of at least 300 MPa.

The dental restorations with the following compositions are further aspects of the present invention:

Composition 1 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 5 SiO₂ 50 to 75 wt-% Li₂O 17 to 20 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 2 SiO₂ 50 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 6 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 3 SiO₂ 55 to 60 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 7 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂ 10 to 15 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 4 SiO₂ 50 to 75 wt-% Li₂O 15 to 22 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 8 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0.1 to 5 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 9 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  1 to 3 wt-% K₂O  0 to 8 wt-% additives  0 to 15 wt-%

Composition 15 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% P₂O₅  1 to 10 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 5 wt-%

Composition 10 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  0.1 to 5 wt-% additives  0 to 15 wt-%

Composition 16 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% P₂O₅  2 to 8 wt-% Al₂O₃  0 to 8 wt-% K₂O  0 to 8 wt-% additives  0 to 7 wt-%

Composition 11 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂  8 to 20 wt-% Al₂O₃  0 to 8 wt-% K₂O  1 to 3 wt-% additives  0 to 15 wt-%

Composition 17 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 4 to 6 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 9 wt-%

Composition 12 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 1 to 10 wt-%

Composition 18 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 13 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 2 to 8 wt-%

Composition 19 SiO₂ 55 to 64 wt-% Li₂O 15 to 22 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 14 SiO₂ 50 to 75 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 4 to 6 wt-%

Composition 20 SiO₂ 55 to 64 wt-% Li₂O 17 to 20 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 24 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 1 to 3 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 25 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0.1 to 5 wt-% additives 0 to 5 wt-%

Composition 21 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 26 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 20 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 1 to 3 wt-% additives 0 to 5 wt-%

Composition 22 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 8 to 15 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0 to 8 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

Composition 23 SiO₂ 55 to 64 wt-% Li₂O 10 to 25 wt-% ZrO₂ 5 to 30 wt-% P₂O₅ 1 to 10 wt-% Al₂O₃ 0.1 to 5 wt-% K₂O 0 to 8 wt-% additives 0 to 5 wt-%

The subject according to the application is intended to be explained in more detail with reference to the subsequent examples without restricting said subject to these variants.

EXAMPLE 1

In Table 1, a fixed compositions given by way of example for different stabilizer is mentioned, from which high stabilizer-containing metasilicate glass ceramics can be produced for the dental field.

TABLE 1 in % by weight SiO₂ 60.0 Li₂O 19.0 P₂O₅ 6.0 Al₂O₃ 2.0 K₂O 2.0 CeO₂ 1.0 Stabilizer SX* 10.0 *SX represent compositions of stabilizers S1 to S5 (s. table 2)

Table 2 shows stabilizers used by way of example for dental applications with the composition of table 1.

TABLE 2 Stabilizers SX S1 Zirconium oxide: 10% S2 Germanium oxide: 10% S3 Lanthanum oxide: 10% S4 Yttrium oxide: 10% S5 Zirconium oxide: 6% Titanium oxide: 4%

The glasses were melted at 1,500° C. and poured into metal moulds to form blocks. The blocks were stressrelieved in the oven at 560° C. and cooled down slowly. For the various characterisation processes, the glass blocks were divided up and subjected to a first crystallisation treatment. For this purpose, the glasses were stored for 10 to 120 minutes at 600° C. to 750° C. As a result of this, glass ceramics with strength values of 150 MPa to 220 MPa were produced. Exclusively lithium metasilicate was hereby established as crystal phase. In this state, processing by means of CAD/CAM methods is possible very readily.

In Table 3, compositions which are given by way of example are mentioned, from which high zirconium oxide-containing metasilicate glass ceramics can be produced for the dental field.

TABLE 3 G1* G2* G3* G4* G5* G6* SiO₂ 63.5 63.5 59.0 59.0 63.5 63.5 Li₂O 12.9 13.9 18.0 19.0 12.9 12.9 ZrO₂ 10.0 9.0 12.0 12.0 12.3 11.0 Al₂O₃ 4.7 5.1 4.5 4.5 3.9 4.4 P₂O₅ 4.5 4.5 3.5 3.5 3.7 4.2 K₂O 4.4 4.0 3.0 2.0 3.6 4.0 *(Data in % by weight)

The glasses were melted at 1,500° C. and poured into metal moulds to form blocks. The blocks were stressrelieved in the oven at 560° C. and cooled down slowly. For the various characterisation processes, the glass blocks were divided up and subjected to a first crystallisation treatment. For this purpose, the glasses were stored for 10 to 120 minutes at 600° C. to 750° C. As a result of this, glass ceramics with strength values of 150 MPa to 220 MPa were produced. Exclusively lithium metasilicate was hereby established as crystal phase. In this state, processing by means of CAD/CAM methods is possible very readily.

EXAMPLE 2

A glass melt with a composition of 60 wt % SiO₂, 19 wt % LiO₂, 10 wt % ZrO₂, 6 wt % P₂O₅, 2 wt % Al₂O₃, 2 wt % K₂O and 2 wt % CeO₂ is cast into a block form. This block is completely crystallized by a two-step firing process. The heat treatment is carried out at 620° C. and 850° C. After this procedure a block holder (e.g. metal attachment) is glued to the block to fix it in a CAM machine.

For this application a dental milling machine (Sirona in Lab MCXL) is used. For a first test the preinstalled parameters for presintered IPS e.max CAD (Software version 3.85) were chosen. A designed anterior crown was milled by using the typical diamond tools. The expected milling time was 17 minutes; the real milling time took 28 min. The chosen burs and the resulting crown showed no problems.

In a second test an identical crown was milled in the same machine by selecting the preinstalled parameters for VITA In-Ceram Spinell. The milling process took also ca. 10 minutes longer than the time calculated. The crown and grinders showed no defects.

After milling the surface of the crown can be optimized by hand. A typical procedure for a dental technician or dentist can be e.g. polishing, glazing, staining and veneering. Bend-bars machined after final crystallizing and treated with a glaze showed fracture values of 370 MPa (3-point-bending strength test conform to DIN EN ISO 6872)

Comparative Test

The commercially available product IPS e.max CAD (Ivoclar-Vivadent, color LT A2) was tested in a comparative way. For this reason the blocks were additionally heat treated at 850° C. The holder, which was removed before final heat treatment, was attached again by gluing.

Then the same crown design was loaded again and the parameters for (normally only partially crystallized) IPS e.max CAD were selected. The complete milling process took ca. 90 minutes instead of the calculated minutes. The process had to be restarted four times because four diamond grinders broke during the process. This shows that it is not possible to machine finally crystallized IPS e.max CAD crowns in a commercially successful way. 

1. A method for producing a dental restoration comprising a lithium silicate glass ceramic, wherein a) an amorphous glass is subjected to at least one heat treatment with temperatures from 450 to 1100° C. resulting in a translucent and tooth coloured and glass ceramic with a strength of at least 250 MPa (measured according to DIN ISO 6872) and with the colour of tooth, wherein during the at least one heat treatment at least a partial crystallisation occurs due to the increased temperatures, and b) the glass ceramic is formed into a dental restoration for immediate dental application and with a strength of at least 200 MPa (measured according to DIN ISO 6872) by a material removing process.
 2. The method of claim 1, wherein the amorphous glass has the following composition: 55 to 70 wt-% SiO₂, 10 to 25 wt % Li₂O, 8 to 20 wt-% of a stabiliser selected from the group consisting of the oxides of Zr, Hf, Ge, La, Y, Ce, Ti, Zn or its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, 0 to 8 wt-% P₂O₅ and 0 to 20 wt-% additives.
 3. The method of claim 1, wherein the heat treatment is a single-stage treatment with a temperature from 600° C. to 950° C. or the heat treatment is a double-stage treatment with a first temperature from 600 to 800° C. and a second temperature from 780 to 900° C.
 4. The method of claim 2, wherein the additives are selected from the group consisting of nucleating agents, fluorescent agents, dyes, glass colouring oxides, coloured pigments, and mixtures thereof.
 5. The method of claim 4, wherein the nucleating agents are selected from the group consisting of phosphorous oxide, titanium oxide, tin oxide, mixtures thereof, and noble metals.
 6. The method of claim 4, wherein the fluorescent agents are selected from oxides of bismuth, rare earth elements neodymium, praseodymium, samarium, europium, terbium, dysprosium, holmium, erbium, and mixtures thereof.
 7. The method of claim 4, wherein the glass colouring oxides are selected from oxides of iron, titanium, cerium, copper, chromium, cobalt, nickel, manganese, selenium, silver, indium, gold, vanadium, rare earth elements, neodymium, praseodymium, samarium, europium, terbium, dysprosium, holmium, erbium, yttrium, and mixtures thereof, and wherein the coloured pigments are doped spinels.
 8. The method of claim 2, wherein the additives are selected from boron oxide, fluorine, barium oxide, strontium oxide, magnesium oxide, zinc oxide, calcium oxide, yttrium oxide, titanium oxide, niobium oxide, tantalum oxide, lanthanum oxide and mixtures thereof.
 9. The method of claim 1, wherein the material removing process is a subtractive process selected from milling, grinding, and laser ablation.
 10. The method of claim 1, wherein before the dental application, the dental restoration is subjected to a finishing process selected from polishing, glazing, sealing, coating, and veneering with a veneering ceramic or glaze.
 11. A translucent and tooth coloured glass ceramic with a strength of at least 250 MPa (measured according to DIN ISO 6872) having the following composition: 55 to 70 wt-% SiO₂, 10 to 25 wt-% Li₂O, 8 to 20 wt-% of a stabiliser selected from Zr, Hf, Ge, La, Y, Ce, Ti, Zn and its mixtures, 0 to 10 wt-% Al₂O₃, 0 to 10 wt-% K₂O and/or Na₂O, and 0 to 20 wt-% additives.
 12. The translucent and tooth coloured glass ceramic of claim 11, which has the following composition: 55 to 64 wt-% SiO₂, 15 to 22 wt-% of Li₂O, 8 to 20 wt-% of a stabiliser selected from ZrO₂, HfO₂ and its mixtures, 0 to 10 wt-% of Al₂O₃, 0 to 10 wt-% of K₂O and/or Na₂O, 0 to 8 wt-% P₂O₅, and 0 to 20 wt-% of additives.
 13. The translucent and tooth coloured glass ceramic of claim 11, wherein the translucent and tooth coloured glass ceramic has a dimensional stability which allows the machining of the translucent and tooth coloured glass ceramic with a material removing process.
 14. A dental restoration produced by the method of claim
 1. 15. The dental restoration of claim 14, wherein the dental restoration has a degree of crystallization of at least 5% and/or the dental restoration has a strength of at least 200 MPa (measured according to DIN ISO 6872).
 16. The dental restoration of claim 13, wherein the dental restoration has a finishing and the finished dental restoration has a strength of at least 250 MPa (measured according to DIN ISO 6872).
 17. The method of claim 2, wherein the amorphous glass has the following composition: 55 to 64 wt-% SiO₂, 15 to 22 wt-% Li₂O, 8 to 20 wt-% of a stabiliser selected from ZrO₂, HfO₂ and mixtures thereof, 0.1 to 8 wt-% Al₂O₃, 0.1 to 8 wt-% K₂O and/or Na₂O, 2 to 8 wt-% P₂O₅, and 0 to 10 wt-% additives.
 18. The method of claim 5, wherein the nucleating agents are present in an amount of 1 to 10 wt-% of the dental restoration.
 19. The method of claim 6, wherein the fluorescent agents are present in an amount of 0.1 to 5 wt-% of the dental restoration.
 20. The method of claim 7, wherein the glass colouring oxides are present in an amount of 0.1 to 6 wt-% of the dental restoration. 